Influence of post-treatment time of trivalent chromium protection coating on aluminium alloy 2024-T3 on improved corrosion resistance
2019
Abstract Low corrosion protection performances of Trivalent Chromium Process (TCP) coatings with reference to Chromium Conversion Coatings (CCC) deposited on aluminium alloys can be overcome by application of post-treatment processes. This work shows the effect of post-treatment bath (containing hydrogen peroxide and lanthanum salt) on the chemical composition, structure and the corrosion performances of TCP coating deposited on AA 2024-T3 aluminium alloy. Different times of post-treatment bath were applied on the TCP coating and the samples were analyzed by Time-of-Flight Secondary Ion Mass Spectrometry (ToF-SIMS), X-ray Photoelectron Spectroscopy (XPS) and Glow Discharge-Optical Emission …
Improvement of the electrochemical behaviour of Zn-electroplated steel using regenerated Cr(III) passivation baths
2014
[EN] Conversion coatings based on trivalent chromium are more sensitive to the presence of zinc and iron impurities than the chromate formulations. This fact contributes to a decrease in the quality of passivation and to the generation of a significant amount of hazardous liquid waste. Recently, a new eco-innovative process based on Emulsion Pertraction Technology (EPT) is being implemented at industrial scale for selectively removing Zn and Fe from spent passivation baths in order to enhance the lifetime of the Cr (III) baths. In this study, the effect of Zn and Fe removal on the electrochemical behaviour of Zn-electroplated steel samples was evaluated by means of polarisation curves and e…
Synthetic and natural chromium bearing spinels: an optical spectroscopy study
2014
Four samples of synthetic chromium-bearing spinels of (Mg, Fe2+)(Cr, Fe3+)2O4 composition and four samples of natural spinels of predominantly (Mg, Fe2+)(Al, Cr)2O4 composition were studied at ambient conditions by means of optical absorption spectroscopy. Synthetic end-member MgCr2O4 spinel was also studied at pressures up to ca. 10 GPa. In both synthetic and natural samples, chromium is present predominantly as octahedral Cr3+ seen in the spectra as two broad intense absorption bands in the visible range caused by the electronic spin-allowed 4A2g → 4T2g and 4A2g → 4T1g transitions (U- and Y-band, respectively). A distinct doublet structure of the Y-band in both synthetic and natural spine…